Common Applications
- Objects used outdoors
- Mechanical functional design testing
- Small gears, casing covers, brackets
- Functional objects, containers
- Automotive accessories
Advantages
- Good heat and weather resistance
- Impact resistant, not easily cracked
- Strong for mechanical loads
- Higher production costs
Disadvantages
- Susceptible to Acetone
Colors
General Specifications
| Property | Value |
|---|---|
| Printing Temperature | 230 - 260°C |
| Bed Temperature | 90 - 110°C |
| Shrinkage Rate | Medium (1.5 - 2.0%) |
Physical Properties
| Property | Test Method | Value |
|---|---|---|
| Density | ISO1183, GB/T1033 | 1.04 g/cm³ at 23°C |
| Melt Index | 220°C, 2.16kg | 9 - 14 g/10min |
| Light Transmission | N/A | N/A |
| Fire Resistance | N/A | N/A |
Chemical Resistance
| Effect | Value |
|---|---|
| Effect from weak acids | Good |
| Effect from strong acids | Poor |
| Effect from weak bases | Good |
| Effect from strong bases | Fair |
| Effect from oils and lubricants | Good |
Thermal Properties
| Property | Test Method | Value |
|---|---|---|
| Glass transition temperature | DSC, 10°C/min | 101°C |
| Melting temperature | DSC, 10°C/min | N/A |
| Crystallization temperature | DSC, 10°C/min | N/A |
| Decomposition temperature | TGA, 20°C/min | >380°C |
| Vicat softening temperature | ISO 306, GB/T 1633 | 104°C |
| Heat deflection temperature | ISO 75 1.8MPa | 98°C |
| Heat deflection temperature | ISO 75 0.45MPa | 100°C |
Mechanical Properties
| Property | Test Method | Value |
|---|---|---|
| Young's Modulus (X-Y) | ISO 527, GB/T 1040 | 2246.6 ± 58.2 MPa |
| Tensile Strength (X-Y) | ISO 527, GB/T 1040 | 33.4 ± 0.6 MPa |
| Elongation at Break (X-Y) | ISO 527, GB/T 1040 | 17.9 ± 1.3 % |
| Flexural Modulus (X-Y) | ISO 178, GB/T 9341 | 2127.2 ± 53.9 MPa |
| Flexural Strength (X-Y) | ISO 178, GB/T 9341 | 56.2 ± 0.3 MPa |
| Charpy Impact Strength (X-Y) | ISO 179, GB/T 1043 | 18.0 ± 0.9 kJ/m² |
Last updated: 6/15/2025